Comparison of the Polymerization Shrinkage of Eclipse Resin for Prostheses with Conventional Acrylic Resins / Comparación de la Contracción de Polimerización de la Resina Eclipse para Prótesis con Resinas Acrílicas Convencionales

ABSTRACT: The objective of this study was to compare the polymerization shrinkage of Eclipse photopolymerization resin for prosthesis based on urethane dimethacrylate (UDMA) with that of three heat-cured acrylic resins based on polymethyl methacrylate (PMMA) after the polymerization process and immersion in water. A total of 40 prostheses were fabricated on a standard metallic upper edentulous model: group 1, Eclipse; group 2, Triplex hot; group 3, Veracril; and group 4, Lucitone 199. Subsequently, the polymerization contraction was tested using a microscope in which measurements were made in micrometres at 3 points located in the middle parts of the right and left sides and the middle part of the palate at three time points once the prosthesis was completed, after 30 days of immersion in water for 8 hours a day at a temperature of 37 °C, and after cutting the prosthesis at the level of the second premolar. ANOVA revealed that the contraction of the polymerization no statistically significant differences between the groups, (P> 0.05). The type of resin and its interaction with the processing method behaves similarly for all test resins. The Veracril heat-cured resin obtained the lowest contraction value in the three measurements (mm) and the highest value was obtained with the Eclipse photopolymerization resin. The Eclipse resin exhibited no lower polymerization shrinkage compared to conventional acrylic resins based on polymethyl methacrylate (PMMA), however it was not significantly affected by immersion in water.

RESUMEN: El objetivo de este estudio fue comparar la contracción de polimerización de la resina de fotopolimerización Eclipse para prótesis basadas en dimetacrilato de uretano (UDMA) con la de tres resinas acrílicas curadas con calor a base de polimetacrilato de metilo (PMMA) después del proceso de polimerización e inmersión en agua. Se fabricaron un total de 40 prótesis en un modelo edéntulo superior metálico estándar: grupo 1, Eclipse; grupo 2, triplex caliente; grupo 3, veracril; y grupo 4, Lucitone 199. Posteriormente, la contracción de la polimerización se probó utilizando un microscopio en el que se realizaron mediciones en micrometros en 3 puntos ubicados en las partes medias de los lados derecho e izquierdo y la parte media del paladar en tres puntos de tiempo una vez la prótesis se completó, después de 30 días de inmersión en agua durante 8 horas al día a una temperatura de 37 °C, y después de cortar la prótesis a nivel del segundo premolar. ANOVA reveló que la contracción de la polimerización no presenta diferencias estadísticamente significativas entre los grupos, (P> 0,05). El tipo de resina y su interacción con el método de procesamiento se comportan de manera similar para todas las resinas de prueba. La resina curada con calor Veracril obtuvo el valor de contracción más bajo en las tres mediciones (mm) y el valor más alto se obtuvo con la resina de fotopolimerización Eclipse. La resina Eclipse no mostró una contracción de polimerización menor en comparación con las resinas acrílicas convencionales basadas en polimetilmetacrilato (PMMA), sin embargo, no se vio afectada significativamente por la inmersión en agua.

Effect of two erosive protocols using acidic beverages on the shear bond strength of orthodontic brackets to bovine enamel

Abstract Objective: To assess the short-term effect of two in vitro erosive challenge protocols on the bond strength of metal orthodontic brackets on bovine enamel. Methods: Sixty bovine incisors were selected and randomly divided into six groups: AS7 (artificial saliva - 7 days, Control Group); CC7 (Coca-Cola™ - 7 days); LJ7 (lime juice - 7 days); AS30 (artificial saliva - 30 days, Control Group); CC30 (Coca-Cola™ - 30 days); LJ30 (lime juice - 30 days). Microhardness testing was performed prior to the erosive challenge to verify the standardization of samples. Immersion was performed 4x/day for five minutes, for either 7 or 30 days. After immersions were concluded, the brackets were bonded and shear bond strength was assessed after 48 hours. The Adhesive Remnant Index (ARI) was also assessed. Data were analyzed by two-way ANOVA, followed by Tukey's post-hoc and Student's t test for paired samples, and the Kruskal-Wallis non-parametric test (α = 5%). Results: The mean and standard deviation of microhardness testing of total samples were 281.89 ± 44.51 KHN. There was no statistically significant difference in shear bond strength for the time factor (7 or 30 days; F5.54= 0.105; p = 0.901). However, there was a statistically significant difference for the solution factor (F5.54= 6.671; p = 0.003). These differences occurred among solutions of Saliva x Coca-Cola™ (p = 0.003) and Coca-Cola™ x Lime Juice (p= 0.029). The assessment of the Adhesive Remnant Index showed no significant difference between groups. Conclusions: The immersion time used in the erosion protocols did not affect the bond strength of brackets to teeth. Coca-Cola™ induced significantly higher shear bond strength values than lime juice and artificial saliva. However, the short term effects of 7/30 days in this in vitro study may not be extrapolated for in vivo ones. Clinical studies should be conducted, substantiating the laboratory results.

Resumo Objetivo: avaliar o efeito de curto prazo de dois protocolos de desafio erosivo, in vitro, na resistência adesiva de braquetes ortodônticos metálicos em esmalte bovino. Métodos: Sessenta incisivos bovinos foram selecionados e divididos aleatoriamente em seis grupos: SA7 (saliva artificial - 7 dias, Grupo Controle); CC7 (Coca-Cola® - 7 dias); SL7 (suco de limão - 7 dias); SA30 (saliva artificial - 30 dias, Grupo Controle); CC30 (Coca-Cola® - 30 dias); SL30 (suco de limão - 30 dias). Foi realizado o teste de microdureza antes do desafio erosivo, para verificar a padronização das amostras. A imersão foi realizada quatro vezes ao dia, por cinco minutos, durante 7 ou 30 dias. Finalizadas as imersões, os braquetes foram colados e, após 48 horas, foi avaliada a resistência ao cisalhamento. O Índice de Adesivo Remanescente (IAR) também foi avaliado. Para análise dos dados, foram utilizados os testes ANOVA dois fatores, seguido do post-hoc de Tukey e teste t de Student para amostras pareadas, e o teste não-paramétrico de Kruskal-Wallis (α?#8197;= 5%). Resultados: a média e o desvio-padrão do teste de microdureza das amostras totais foi igual a 281,89 ± 44,51 KHN. Não houve diferença estatisticamente significativa na resistência ao cisalhamento para o fator tempo (7 ou 30 dias; F5,54= 0,105; p= 0,901). Contudo, houve diferença estatisticamente significativa para o fator solução (F5,54=6,671; p= 0,003). Essas diferenças ocorreram entre as soluções de Saliva x Coca-Cola® (p= 0,003) e Coca-Cola® x suco de limão (p= 0,029). Ao avaliar o Índice de Adesivo Remanescente, não foi possível verificar diferença significativa entre os grupos. Conclusões: o tempo de imersão utilizado nos protocolos de erosão não afetou a resistência de união dos braquetes aos dentes. A Coca-Cola® induziu valores de resistência ao cisalhamento significativamente mais altos do que o suco de limão e a saliva artificial. No entanto, os efeitos em curto prazo de 7 e 30 dias, nesse estudo in vitro, não podem ser extrapolados para os estudos in vivo. Estudos clínicos devem ser conduzidos, fundamentando os resultados laboratoriais.

Polymerization shrinkage stress of composite resins and resin cements - What do we need to know?

Abstract Polymerization shrinkage stress of resin-based materials have been related to several unwanted clinical consequences, such as enamel crack propagation, cusp deflection, marginal and internal gaps, and decreased bond strength. Despite the absence of strong evidence relating polymerization shrinkage to secondary caries or fracture of posterior teeth, shrinkage stress has been associated with post-operative sensitivity and marginal stain. The latter is often erroneously used as a criterion for replacement of composite restorations. Therefore, an indirect correlation can emerge between shrinkage stress and the longevity of composite restorations or resin-bonded ceramic restorations. The relationship between shrinkage and stress can be best studied in laboratory experiments and a combination of various methodologies. The objective of this review article is to discuss the concept and consequences of polymerization shrinkage and shrinkage stress of composite resins and resin cements. Literature relating to polymerization shrinkage and shrinkage stress generation, research methodologies, and contributing factors are selected and reviewed. Clinical techniques that could reduce shrinkage stress and new developments on low-shrink dental materials are also discussed.

Prototype to measure bracket debonding force in vivo

ABSTRACT Introduction: Material biodegradation that occurs in the mouth may interfere in the bonding strength between the bracket and the enamel, causing lower bond strength values in vivo, in comparison with in vitro studies. Objective: To develop a prototype to measure bracket debonding force in vivo and to evaluate, in vitro, the bond strength obtained with the prototype. Methods: A original plier (3M Unitek) was modified by adding one strain gauge directly connected to its claw. An electronic circuit performed the reading of the strain gauge, and the software installed in a computer recorded the values of the bracket debonding force, in kgf. Orthodontic brackets were bonded to the facial surface of 30 bovine incisors with adhesive materials. In Group 1 (n = 15), debonding was carried out with the prototype, while tensile bond strength testing was performed in Group 2 (n = 15). A universal testing machine was used for the second group. The adhesive remnant index (ARI) was recorded. Results: According to Student’s t test (α = 0.05), Group 1 (2.96 MPa) and Group 2 (3.08 MPa) were not significantly different. ARI score of 3 was predominant in the two groups. Conclusion: The prototype proved to be reliable for obtaining in vivo bond strength values for orthodontic brackets.

RESUMO Introdução: a biodegradação de materiais que ocorre na cavidade bucal pode interferir na resistência de união entre o braquete e o esmalte, causando baixos valores de resistência de união in vivo, em comparação aos valores in vitro. Objetivo: o objetivo do presente estudo foi desenvolver um protótipo para mensurar, in vivo, a força de descolagem de braquetes e avaliar, in vitro, a resistência de união obtida com o uso do protótipo. Métodos: um alicate (3M Unitek) foi modificado por meio da adição de um extensômetro diretamente conectado à garra do alicate. Um circuito eletrônico realizou a leitura do extensômetro, e um software instalado em um computador registrou os valores de força de descolagem do braquete em kgf. Os braquetes ortodônticos foram colados com material adesivo na face vestibular de 30 dentes incisivos bovinos. No Grupo 1 (n = 15), a descolagem foi realizada com o protótipo, enquanto no Grupo 2 (n = 15) foi realizado teste de resistência de união à tração, utilizando-se uma máquina universal de ensaios. O índice de adesivo remanescente (ARI) foi analisado. Resultados: de acordo com o teste de t de Student (α = 0,05), os grupos 1 (2,96 MPa) e 2 (3,08 MPa) não foram estatisticamente diferentes. O escore 3 do ARI foi predominante nos dois grupos. Conclusão: o protótipo mostrou-se confiável para se obter, in vivo, os valores de resistência de união dos braquetes ortodônticos.

Four chemical methods of porcelain conditioning and their influence over bond strength and surface integrity

OBJECTIVE: To assess four different chemical surface conditioning methods for ceramic material before bracket bonding, and their impact on shear bond strength and surface integrity at debonding.METHODS: Four experimental groups (n = 13) were set up according to the ceramic conditioning method: G1 = 37% phosphoric acid etching followed by silane application; G2 = 37% liquid phosphoric acid etching, no rinsing, followed by silane application; G3 = 10% hydrofluoric acid etching alone; and G4 = 10% hydrofluoric acid etching followed by silane application. After surface conditioning, metal brackets were bonded to porcelain by means of the Transbond XP system (3M Unitek). Samples were submitted to shear bond strength tests in a universal testing machine and the surfaces were later assessed with a microscope under 8 X magnification. ANOVA/Tukey tests were performed to establish the difference between groups (α= 5%).RESULTS: The highest shear bond strength values were found in groups G3 and G4 (22.01 ± 2.15 MPa and 22.83 ± 3.32 Mpa, respectively), followed by G1 (16.42 ± 3.61 MPa) and G2 (9.29 ± 1.95 MPa). As regards surface evaluation after bracket debonding, the use of liquid phosphoric acid followed by silane application (G2) produced the least damage to porcelain. When hydrofluoric acid and silane were applied, the risk of ceramic fracture increased.CONCLUSIONS: Acceptable levels of bond strength for clinical use were reached by all methods tested; however, liquid phosphoric acid etching followed by silane application (G2) resulted in the least damage to the ceramic surface.

OBJETIVO: avaliar quatro métodos de condicionamento químico da superfície cerâmica, previamente à colagem de braquetes, e seu impacto sobre a resistência ao cisalhamento e a integridade da superfície ao descolamento.MÉTODOS: quatro grupos experimentais (n = 13) foram delineados de acordo com o método de condicionamento da superfície cerâmica empregado: G1 = ácido fosfórico a 37%, seguido da aplicação de silano; G2 = ácido fosfórico líquido a 37%, seguido da aplicação de silano sem lavagem prévia do ácido; G3 = ácido fluorídrico a 10%; e G4 = ácido fluorídrico a 10%, seguido da aplicação de silano. Após o condicionamento da superfície, braquetes metálicos foram colados à porcelana utilizando-se o sistema Transbond XP (3M Unitek). As amostras foram submetidas a ensaios de resistência ao cisalhamento, em máquina de ensaio universal, e as superfícies cerâmicas foram posteriormente avaliadas em microscópio, com magnitude de 8X. Testes ANOVA/Tukey foram realizados para verificar-se a diferença entre os grupos (α = 5%).RESULTADOS: os maiores valores de resistência ao cisalhamento foram encontrados nos grupos G3 e G4 (22,01 ± 2,15MPa e 22,83 ± 3,32Mpa, respectivamente), seguidos por G1 (16,42 ± 3,61MPa) e G2 (9,29 ± 1,95MPa). Quanto à avaliação da superfície após a descolagem do braquete, a utilização de ácido fosfórico líquido seguido da aplicação de silano, sem lavagem do ácido (G2), produziu menores danos à porcelana. Quando ácido fluorídrico e silano foram aplicados, o risco de fraturar a cerâmica aumentou.CONCLUSÕES: níveis aceitáveis de resistência de união para uso clínico foram alcançados por todos os métodos testados. No entanto, o condicionamento com ácido fosfórico líquido, seguido da aplicação de silano (G2), resultou em menor dano à superfície cerâmica.

Evaluation of stiffness and plastic deformation of active ceramic self-ligating bracket clips after repetitive opening and closure movements

OBJECTIVE: The aim of this study was to assess whether repetitive opening and closure of self-ligating bracket clips can cause plastic deformation of the clip.METHODS: Three types of active/interactive ceramic self-ligating brackets (n = 20) were tested: In-Ovation C, Quicklear and WOW. A standardized controlled device performed 500 cycles of opening and closure movements of the bracket clip with proper instruments and techniques adapted as recommended by the manufacturer of each bracket type. Two tensile tests, one before and one after the repetitive cycles, were performed to assess the stiffness of the clips. To this end, a custom-made stainless steel 0.40 x 0.40 mm wire was inserted into the bracket slot and adapted to the universal testing machine (EMIC DL2000), after which measurements were recorded. On the loading portion of the loading-unloading curve of clips, the slope fitted a first-degree equation curve to determine the stiffness/deflection rate of the clip.RESULTS: The results of plastic deformation showed no significant difference among bracket types before and after the 500 cycles of opening and closure (p = 0.811). There were significant differences on stiffness among the three types of brackets (p = 0.005). The WOW bracket had higher mean values, whereas Quicklear bracket had lower values, regardless of the opening/closure cycle.CONCLUSION: Repetitive controlled opening and closure movements of the clip did not alter stiffness or cause plastic deformation.

OBJETIVO: o objetivo deste estudo foi avaliar se a abertura e o fechamento repetitivo do clipe de braquetes autoligáveis podem causar deformação plástica do clipe.MÉTODOS: três tipos de braquetes autoligáveis ativos/interativos estéticos (n = 20) foram testados: In-Ovation C, Quicklear e WOW. Um dispositivo realizou, de forma controlada e padronizada, 500 ciclos de abertura e de fechamento do clipe, com instrumentos e técnicas adequadas, tal como recomendado pelo fabricante de cada tipo de braquete. Dois ensaios de tração, um antes e um depois dos ciclos repetitivos, foram realizados para se avaliar a rigidez dos clipes. Para o ensaio de tração, um fio de 0,40 x 0,40mm de aço inoxidável foi inserido no slot do braquete e adaptado em uma máquina universal de ensaios (EMIC DL2000), sendo as medições registradas. Na porção retilínea da curva de carregamento dos clipes, a inclinação é definida por uma equação de primeiro grau, determinando o coeficiente de elasticidade (rigidez) do clipe.RESULTADOS: os resultados quanto à deformação plástica não mostraram nenhuma diferença significativa entre os tipos de braquetes, antes e depois dos 500 ciclos de abertura e de fechamento (p = 0,811). Foram encontradas diferenças significativas na rigidez entre os três tipos de braquetes (p = 0,005): o braquete WOW demonstrou valores médios mais elevados, e o braquete Quicklear demonstrou valores mais baixos, independentemente do ciclo de abertura e fechamento.CONCLUSÃO: movimentos repetitivos controlados de abertura e de fechamento do clipe não alteraram a rigidez ou causaram deformação plástica.

Load-Application Devices: A Comparative Strain Gauge Analysis

In view of the low loading values commonly employed in dentistry, a load-application device (LAD) was developed as option to the universal testing machine (UTM), using strain gauge analysis. The aim of this study was to develop a load-application device (LAD) and compare the LAD with the UTM apparatus under axial and non-axial loads. An external hexagonal implant was inserted into a polyurethane block and one EsthetiCone abutment was connected to the implant. A plastic prosthetic cylinder was screwed onto the abutment and a conical pattern crown was fabricated using acrylic resin. An impression was made and ten identical standard acrylic resin patterns were obtained from the crown impression, which were cast in nickel-chromium alloy (n=10). Four strain gauges were bonded diametrically around the implant. The specimens were subjected to central (C) and lateral (L) axial loads of 30 kgf, on both devices: G1: LAD/C; G2: LAD/L; G3: UTM/C; G4: UTM/L. The data (με) were statistically analyzed by repeated measures ANOVA and Tukey's test (p<0.05). No statistically significant difference was found between the UTM and LAD devices, regardless of the type of load. It was concluded that the LAD is a reliable alternative, which induces microstrains to implants similar to those obtained with the UTM.

Considerando os valores relativamente pequenos utilizados em odontologia para os ensaios de carregamento verticais axiais, foi desenvolvido um dispositivo de aplicação de carga (DAC) para substituir a máquina de ensaios universal (EMIC). O objetivo deste estudo foi desenvolver um DAC e compará-lo com a EMIC por meio da utilização de carregamentos axiais e não-axiais. Num bloco de poliuretano foi inserido um implante hexágono externo, o qual foi conectado a um pilar protético esteticone. Sobre o pilar protético foi parafusada uma coifa plástica e um pilar cônico foi modelado em resina acrílica, que foi moldada para a obtenção de dez enceramentos iguais que foram fundidos em níquel cromo. Quatro extensômetros foram diametralmente colados ao redor do implante. Cada corpo de prova foi submetido a cargas axiais central (C) e lateral (L) de 30 kgf, em ambos os dispositivos: G1) DAC/C; G2) DAC/L; G3) EMIC/C; G4) EMIC/L. Os dados (µε) foram analisados estatisticamente pelos testes de ANOVA para medidas repetidas e de Tukey (p<0,05). Não houve diferença estatisticamente significante entre os dispositivos DAC e EMIC, independente do tipo de carga. A aplicação de carga não-axial (NA) determinou um aumento significante de tensões ao redor do implante. Foi concluído que o DAC é uma opção confiável, a qual induz microtensão em implantes de forma semelhante à EMIC.

Evaluation of bond strenght between leucite-based and lithium disilicate-based ceramics to dentin after cementation with conventional and self-adhesive resin agents

The aim of this study was to compare the microtensile bondstrength of two heat-pressed ceramics (leucite-based - IPSEmpress Esthetic/ Ivoclar Vivadent, and lithium disilicate-based- IPS e.max Press/ Ivoclar Vivadent) to dentin with the use ofconventional and self-adhesive resin cements. The occlusal surfaceof 60 intact human molars was removed and the dentin wasexposed. Ceramic blocks were cemented randomly with regardto the cementation systems (n=10): conventional dual resincement (Variolink II/ Ivoclar Vivadent), conventional self-polymerizingresin cement (Multilink/ Ivoclar Vivadent), and dualself-adhesive resin cement (RelyX U100/ 3M ESPE). The dualcementation systems were photoactivated with a LED lightdevice (Radii Cal, SDI) for 40 seconds. The specimens were sectionedto obtain sticks of approximately 1 mm2 for microtensiletests on a universal testing machine (EMIC). The type of fracturewas analyzed under a scanning electron microscope. TheAnalysis of Variance (ANOVA) and the Tukey test (α=0.05)showed that there was no difference between types of ceramic.Average microtensile bond strength was higher for the conventionaldual resin cement (Variolink II) and the self-adhesive dualresin cement (RelyX U100), despite greater prevalence of prematureloss of the sticks with the latter. Average bond strengthwas lower when the conventional self-polymerizing resin cement(Multilink) was used. Leucite-based and lithium disilicate-basedcements present similar bond strength to the dentin withconventional dual resin cement (Variolink II) and a dual selfadhesivecement (RelyX U100)...

O objetivo deste estudo foi avaliar a resistência de união pormicrotração à dentina humana entre cerâmicas prensadas (abase de leucita - IPS Empress Esthetic/ Ivoclar Vivadent, e abase de dissilicato de lítio - IPS e.max Press/ Ivoclar Vivadent)após cimentação com agentes resinosos e convencionais eautoadesivos. As superfícies oclusais de 60 molares humanoshígidos foram removidas e a dentina foi exposta. A cimentaçãodos blocos cerâmicos foi realizada de forma aleatória de acordocom os sistemas de cimentação (n=10): cimento resinosodual convencional (Variolink II/ Ivoclar Vivadent), cimentoresinoso autopolimerizável convencional (Multilink/ IvoclarVivadent) e cimento resinoso dual autoadesivo (RelyX U100/3M ESPE). Os sistemas de cimentação duais foram fotoativadoscom aparelho de luz LED (Radii Cal, SDI) por 40segundos. Os espécimes foram seccionados para a obtençãode palitos com aproximadamente 1 mm2 para a realização doteste de microtração em máquina universal de ensaios (EMIC).O padrão de fratura foi analisado em microscópio eletrônicode varredura. A Análise de Variância (ANOVA) e o teste deTukey (α=0,05) mostraram que não houve diferenças entre ostipos de cerâmicas. Houve maiores médias de resistência deunião por microtração para o cimento resinoso dual convencional(Variolink II) e para cimento resinoso dual autoadesivo(RelyX U100), apesar de maior prevalência de perdas prematurasdos palitos com este cimento. Houve menores médias deresistência de união ao se utilizar o cimento resinoso autopolimerizávelconvencional (Multilink). As cerâmicas a base deleucita (IPS Empress Esthetic) e a base de dissilicato de lítio(IPS e.max Press) apresentaram resistência de união semelhanteà dentina ao se utilizar o cimento resinoso dualconvencional (Variolink II) e o dual autoadesivo (RelyX U100)...

Comparative study of friction between metallic and conventional interactive self-ligating brackets in different alignment conditions

OBJECTIVE: The aim of this study was to compare the friction between three bracket models: conventional stainless steel (Ovation, Dentsply GAC), self-ligating ceramic (In-Ovation, Denstply GAC) and self-ligating stainless steel brackets (In-Ovation R, Dentsply GAC). METHODS: Five brackets were used for each model. They were bonded to an aluminum prototype that allowed the simulation of four misalignment situations (n = 10). Three of these situations occurred at the initial phase (in which a 0.016-in nickel-titanium wire was used): 1. horizontal; 2. vertical; and 3. simultaneous horizontal/vertical. One of the situations occurred at the final treatment phase: 4. no misalignment (in which a 0.019 x 0.025-inch stainless steel rectangular wire was used). The wires slipped through the brackets and friction was measured by a Universal Testing Machine. RESULTS: Analysis of variance followed by Tukey's Test for multiple comparisons (α = 0.05) were applied to assess the results. Significant interaction (p < 0.01) among groups was found. For the tests that simulated initial alignment, Ovation(r) bracket produced the highest friction. The two self-ligating models resulted in lower and similar values, except for the horizontal situation, in which In-Ovation C(r) showed lower friction, which was similar to the In-Ovation R(r) metallic model. For the no misalignment situation, the same results were observed. CONCLUSION: The self-ligating system was superior to the conventional one due to producing less friction. With regard to the material used for manufacturing the brackets, the In-Ovation C(r) ceramic model showed less friction than the metallic ones. .

OBJETIVO: o objetivo desse trabalho in vitro foi comparar o atrito entre três modelos de braquetes: Ovation (convencional, aço inoxidável); In-Ovation C (autoligável, cerâmico) e In-Ovation R (autoligável, aço inoxidável), todos do mesmo fabricante (Dentsply GAC). MÉTODOS: para cada modelo, foram utilizados cinco braquetes, colados a um protótipo de alumínio, que permitiu a simulação de quatro situações (n = 10), sendo uma delas sem desalinhamento (com utilização de fio retangular de aço inoxidável, com espessuras de 0,019" x 0,025") e outras três com desalinhamento, sendo um horizontal, um vertical e outro simultaneamente combinando ambos (com utilização de fio de níquel-titânio com espessura de 0,016"). O atrito foi mensurado por uma máquina universal de ensaios. RESULTADOS: os resultados obtidos foram submetidos ao teste de Análise de Variância, complementado pelo teste de comparações múltiplas de Tukey (α = 0,05). Foi observada interação significativa entre os grupos (p < 0,01). Para os ensaios que simularam a fase inicial de alinhamento, realizada com fios de NiTi, o braquete Ovation foi o que produziu o maior atrito, e os dois modelos autoligáveis produziram resultados menores e semelhantes, exceto para o ensaio de desalinhamento horizontal, onde o In-Ovation C apresentou atrito menor do que o similar metálico In-Ovation R. Na fase em que o fechamento de espaço foi simulado, os mesmos resultados foram observados. CONCLUSÃO: pode-se concluir que o sistema de autoligável mostrou-se superior ao convencional, com elastômeros, por produzir menor atrito. Quanto ao material utilizado na confecção dos braquetes, o modelo cerâmico In-Ovation C apresentou menor atrito que os metálicos. .

Comparison of frictional resistance between self-ligating and conventional brackets tied with elastomeric and metal ligature in orthodontic archwires

OBJECTIVE: To compare the frictional resistance between self-ligating and conventional brackets tied to different types of wire. MATERIAL AND METHODS : Abzil Kirium Capelozza (Pattern I) and Easy Clip (Roth prescription) incisor brackets were used. An elastomeric ligature or a ligating wire 0.10-in was used to ligate the wire to the Abzil bracket. Three types of orthodontic archwire alloys were assessed: 0.016-in NiTi wire, 0.016 x 0.021-in NiTi wire and 0.019 x 0.025-in steel wire. Ten observations were carried out for each bracket-archwire angulation combination. Brackets were mounted in a special appliance, positioned at 90 degrees in relation to the wire and tested in two angulations. Frictional test was performed in a Universal Testing Machine at 5 mm/min and 10 mm of displacement. The means (MPa) were submitted to ANOVA and Tukey's test set at 5% of significance. The surfaces of wires and brackets were observed at SEM. RESULTS: Steel-tied brackets (16.48 ± 8.31) showed higher means of frictional resistance than elastomeric-tied brackets (4.29 ± 2.16 ) and self-ligating brackets (1.66 ± 1.57) (P < 0.05), which also differed from each other (P < 0.05). As for the type of wire, 0.019 x 0.025-in steel wire (5.67 ± 3.97) showed lower means (P < 0.05) than 0.16-in NiTi wire (8.26 ± 10.92) and 0.016 x 0.021-in NiTi wire (8.51 ± 7.95), which did not differ from each other (P > 0.05). No statistical differences (P > 0.05) were found between zero (7.76 ± 8.46) and five-degree (7.19 ± 7.93) angulations. CONCLUSIONS: Friction was influenced not only by the type of bracket, but also by the ligating systems. Different morphological aspects were observed for the brackets and wires studied .

OBJETIVO: comparar a resistência ao atrito entre braquetes autoligáveis e braquetes convencionais, variando o tipo de fio. MÉTODOS: foram usados braquetes incisivos Abzil Kirium Capelozza e Easy Clip. Uma ligadura elastomérica ou um fio ligável de 0,010" foi usado para ligação do fio no braquete Abzil. Três tipos de ligas de fio ortodôntico foram avaliadas: fio de NiTi de 0,016"; fio de NiTi de 0,016" x 0,022"; e fio de aço de 0,019" x 0,025". Dez observações foram feitas para cada combinação "braquete-fio-inclinação". Os braquetes foram montados em um aparelho especial, posicionados a 90° em relação ao fio, e testados em duas inclinações. O teste de atrito foi realizado na máquina universal de ensaios, a 5mm/min e com 10mm de deslocamento. As médias (em MPa) foram submetidas aos testes ANOVA e de Tukey, a 5% de significância. As superfícies dos fios e dos braquetes foram observadas no MEV. RESULTADOS: o braquete com amarrilhos metálicos (16,48 ± 8,31MPa) apresentou médias mais altas que o braquete com ligaduras elastoméricas (4,29 ± 2,16MPa) e o braquete autoligável (1,66 ± 1,57) (p < 0,05), os quais também diferiram entre si (p < 0,05). Quanto ao tipo do fio, o fio de aço de 0,019" x 0,025" (5,67 ± 3,97MPa) apresentou médias mais baixas (p < 0,05) que os fios de NiTi de 0,016" (8,26 ± 10,92MPa) e de 0,016" x 0,022" (8,51 ± 7,95), os quais não diferiram entre si (p > 0,05). Nenhuma diferença estatística (p > 0,05) foi encontrada entre inclinações de zero (7,76 ± 8,46) e cinco (7,19 ± 7,93) graus. Concluão: o atrito foi influenciado pelo tipo de braquete e sistemas de ligaduras. Diferentes aspectos morfológicos foram observados para os braquetes e fios estudados. .

Shear bond resistance and enamel surface comparison after the bonding and debonding of ceramic and metallic brackets

OBJECTIVE: To evaluate, in vitro, the shear bond strength presented by three brands of polycrystalline ceramic brackets and one brand of metallic bracket; verify the adhesive remnant index (ARI) after the tests, and analyze, through scanning electron microscopy (SEM) the enamel surface topography after debonding, detecting the release of mineral particles. METHODS: Sixty bovine lower incisors were used. Three ceramic brackets (Allure(r), InVu(r), and Clarity(r)) and one metallic bracket (Geneus(r)) were bonded with Transbond XT(r). Kruskal-Wallis's test (significance level set at 5%) was applied to the results of share bond and ARI. Mann Whitney's test was performed to compare the pairs of brackets in relation to their ARI. Brown-Forsythe's test (significance level set at 5%) was applied to the results of enamel chemical composition. Comparisons between groups were made with Games-Howell's and the Post-hoc tests. RESULTS: No statistically significant difference was observed in relation to the shear bond strength loads. Clarity(r) brackets were the most affected in relation to the surface topography and to the release of mineral particles of enamel (calcium ions). CONCLUSION: With regard to the ARI, there was a prevalence of score 4 (40.4%). As for enamel surface topography, the Geneus(r) bracket was the only one which did not show superficial tissue loss. The InVu(r) and Clarity(r) ones showed cohesive fractures in 33.3% and the Allure(r) in 50%, the latter being the one that presented most fractures during removal. .

OBJETIVO: avaliar, in vitro, a resistência ao cisalhamento apresentada por três marcas de braquetes ortodônticos cerâmicos policristalinos e uma marca de braquete metálico, verificando os índices de resina remanescentes (IRA) após os ensaios, e analisar, por meio de microscopia eletrônica de varredura, as topografias superficiais do esmalte após a descolagem, detectando o desprendimento de partículas minerais desse. MÉTODOS: foram utilizados 60 incisivos inferiores bovinos. Os braquetes cerâmicos (Allure, InVu e Clarity) e metálico (Geneus) foram colados utilizando-se o adesivo Transbond XT. Para os resultados referentes ao cisalhamento e ao IRA, foi utilizado o teste de Kruskal-Wallis, com nível de significância de 5%. A prova de Mann-Whtiney foi utilizada para comparar os diferentes tipos de braquetes aos pares, quanto ao IRA. Para a análise dos resultados referentes às composições químicas do esmalte, aplicou-se o teste de Brown-Forsythe, com significância de 5%. As comparações entre os grupos foram realizadas utilizando os testes Post Hoc e de Games-Hoewell. RESULTADOS: não foram observadas diferenças significativas quanto às cargas de cisalhamento. O Clarity foi o mais afetado em relação à topografia e ao desprendimento de partículas minerais do esmalte (íons Ca). CONCLUSÃO: em relação ao IRA, foi confirmada a prevalência do escore 4, com um percentual de 40,4%. Em relação à topografia superficial do esmalte, o Geneus foi o único que não apresentou perda de tecido . O InVu e o Clarity apresentaram fraturas coesivas de 33,3% de suas amostras, e o Allure de 50%, sendo o que mais fraturou durante a remoção. .

Comparison of friction produced by two types of orthodontic bracket protectors

INTRODUCTION: Fixed orthodontic appliances have been regarded as a common causative factor of oral lesions. To manage soft tissue discomfort, most orthodontists recommend using a small amount of utility wax over the brackets in order to alleviate trauma. This in vitro study aimed at evaluating friction generated by two types of bracket protectors (customized acetate protector [CAP] and temporary resin protector [TRP]) during the initial stages of orthodontic treatment. METHODS: An experimental model (test unit) was used to assess friction. In order to measure the friction produced in each test, the model was attached to a mechanical testing machine which simulated maxillary canines alignment. Intergroup comparison was carried out by one-way ANOVA with level of significance set at 5%. RESULTS: The friction presented by the TRP group was statistically higher than that of the control group at 6 mm. It was also higher than in the control and CAP groups in terms of maximum friction. CONCLUSION: The customized acetate protector (CAP) demonstrated not to interfere in friction between the wire and the orthodontic bracket slot. .

INTRODUÇÃO: o aparelho ortodôntico fixo é considerado um fator causador de traumas na mucosa bucal. Com o intuito de controlar o desconforto no tecido mole, diversos ortodontistas recomendam a utilização de uma pequena quantidade de cera utilidade sobre os braquetes como forma de proteção. Esse estudo teve como objetivo avaliar, in vitro, o atrito gerado por dois tipos de protetores de braquetes (protetor de acetato e de resina - PPA e PRT) durante os estágios iniciais do tratamento ortodôntico. MÉTODOS: o atrito gerado pelos protetores no fio ortodôntico foi avaliado em unidades de teste de modelos experimentais. Esses modelos foram ligados a uma máquina de ensaios mecânicos que simulava o alinhamento do canino superior. A comparação intergrupos foi realizada pela ANOVA, com nível de significância de 5%. RESULTADOS: a fricção apresentada pelo grupo PRT foi estatisticamente maior do que a do grupo controle ao nível de 6mm. Para o atrito máximo, a média do grupo PRT foi estatisticamente maior do que a dos grupos controle e PPA. CONCLUSÃO: o protetor de acetato demonstrou não interferir no atrito entre o fio e a ranhura do braquete ortodôntico. .

Effect of Two Microshear Test Devices on Bond Strength and Fracture Pattern in Primary Teeth

This in vitro study evaluated the influence of two devices for application of shear load in microshear tests on bond strength and fracture pattern of primary enamel and dentin. Eighty primary molars were selected and flat enamel (40 teeth sectioned mesio-distally) and dentin (40 teeth sectioned transversally) surfaces were obtained. Both surfaces were polished to standardize the smear layer. Two-step etch-and-rinse adhesive systems (Adper Single Bond and XP Bond) were used. Polyethylene tubes was placed over the bonded surfaces and filled with composite resin. The microshear testing was performed after storage in water (24 h/37 °C) using two devices for application of microshear loads: a notched rod (Bisco Shear Bond Tester) or a knife edge (Kratos Industrial Equipment). Failure modes were evaluated using a stereomicroscope. Bond strength data were subjected to ANOVA and chi-square test to compare the failure mode distributions (α=0.05). No significant differences were observed between the groups for dentin and enamel bond strength or fracture patterns (p>0.05). The predominant failure mode was adhesive/mixed. In conclusion, the devices for application of shear loads did not influence the bond strength values, regardless of adhesive system and substrate.

Este estudo in vitro avaliou a influência de dois dispositivos para aplicação de força de cisalhamento em testes de resistência de união ao microcisalhamento e no padrão de fratura em dentina e esmalte de dentes decíduos. Oitenta molares decíduos foram selecionados e superficies planas em esmalte (40 dentes seccionados no sentido mésio-distal) e dentina (40 dentes seccionados transversalmente) foram obtidas. Ambas as superficies foram abrasionadas para padronização da lama dentinária. Dois sistemas adesivos de condicionamento ácido prévio (Adper Single Bond e XP Bond) foram utilizados. Tubos de polietileno foram colocados sobre as superficies, nas quais já haviam sido aplicados os sistemas adesivos, e preenchidos com resina composta. O teste de resistência de união ao microcisalhamento foi realizado após armazenamento dos espécimes em água (24 h/37 °C) utilizando dois dispositivos para a aplicação das forças de cisalhamento: cisalha côncava (Bisco Shear Bond Tester) e cisalha plana (Kratos Industrial Equipment). O padrão de fratura foi avaliado usando estereomicroscópio. Os dados de resistência de união foram submetidos à ANOVA e o teste quiquadrado foi utilizado para comparar a distribuição dos padrões de fratura (α=0,05). Não foram observadas diferenças estatisticamente significantes entre os grupos, tanto para a resistência de união a dentina e esmalte quanto para o padrão de fratura (p>0,05). O modo de falha predominante foi adesiva/mista. Em conclusão, os dispositivos para aplicação de força de cisalhamento não influenciam os valores de resistência de união, independente do sistema adesivo e substrato.

Prototype of a new tip developed to be coupled to dental light-curing units for optimizing bonding of orthodontic brackets and accessories

OBJECTIVE: development of a new device to be coupled to light-curing units for bonding orthodontic brackets and accessories, and test its efficacy in an in vitro mechanical trial. The inner surface of the device is mirrored and is based on physical concepts of light refraction and reflection. The main advantage of such device is the reduced clinical time needed for bonding and the low possibility of contamination during the process. METHODS: One hundred and twenty specimens were used for testing the shear bond strength of brackets bonded with the device. The Adhesive Remnant Index (ARI) was also determined. The sample was divided into 2 groups. In group 1 a halogen light-curing unit was used while in group 2 a led light-curing unit was used. Each group was then subdivided. In subgroups H1 and L1, a conventional light guide rod was used while in subgroups H2 and L2 bonding was performed with the mirrored device coupled to the tip of the guide light rod. RESULTS: The values obtained for the shear bond strength and the ARI in the subgroups were compared. Results showed that there was no statistically significant difference for the shear strength (p > 0.05) and the ARI (p > 0.05) between the subgroups. CONCLUSION: The tests of mechanical trials and the ARI analysis showed that the new device fulfilled the requirements for bonding orthodontic accessories, and that the time for bonding was reduced to half, being necessary only one light exposure.

OBJETIVO: desenvolver uma nova ponteira para ser acoplada aos aparelhos fotopolimerizadores utilizados para colagem de braquetes e acessórios ortodônticos, e testar sua da efetividade em ensaio mecânico in vitro. A ponteira é espelhada na superfície interna e baseia-se em conceitos físicos de refração e reflexão de luz. Apresenta como principal vantagem o menor tempo clínico durante o procedimento de colagem, reduzindo a possibilidade de contaminação durante o processo. MÉTODOS: por meio de ensaio de resistência ao cisalhamento e determinação do índice remanescente de adesivo (IRA), testou-se a ponteira desenvolvida em 120 corpos de prova. A amostra foi dividia em dois grupos. No grupo 1, foi utilizado aparelho fotopolimerizador de fonte de luz halógena e, no grupo 2, fonte de LED. Cada grupo foi subdividido. Nos subgrupos H1 e L1, utilizou-se a ponteira convencional. Nos subgrupos H2 e L2 a colagem foi feita utilizando a ponteira desenvolvida para a polimerização do material de colagem. RESULTADOS: os valores dos testes de cisalhamento e IRA para os subgrupos foram comparados entre si. Os resultados mostraram que não houve diferença estatisticamente significativa para o ensaio de resistência ao cisalhamento (p > 0,05) nem para o IRA (p > 0,05) entre os subgrupos. CONCLUSÃO: os testes de ensaio mecânico, assim como a análise do IRA, mostraram que a nova ponteira desenvolvida cumpriu os requisitos necessários à colagem dos acessórios ortodônticos, e que o tempo de colagem foi reduzido pela metade, sendo necessária uma só incidência.

Flexural strength of mini-implants developed for Herbst appliance skeletal anchorage: a study in Minipigs br1 cadavers

OBJECTIVE: The present study was designed to verify if mini-implant prototypes (MIP) developed for Herbst appliance anchorage are capable of withstanding orthopedic forces, and to determine whether the flexural strength of these MIP varies depending on the site of insertion (maxilla and mandible). METHODS: Thirteen MIP were inserted in three minipig cadavers (six in the maxilla and seven in the mandible). The specimens were prepared and submitted to mechanical testing. The mean and standard deviation were calculated for each region. A two-way Student's t test was used to compare the strength between the sites. A one-way Student's t test was performed to test the hypothesis. Orthopedic forces above 1.0 kgf were considered. RESULTS: The MIP supported flexural strength higher than 1.0 kgf (13.8 ± 2.3 Kg, in the posterior region of the maxilla and 20.5 ± 5.2 Kg in the anterior region of the mandible) with a significantly lower flexural strength in the anterior region of the mandible (P < 0.05). CONCLUSION: The MIP are capable of withstanding orthopedic forces, and are more resistant in the anterior region of the mandible than in the posterior region of the maxilla in Minipigs br1 cadavers.

OBJETIVO: o presente estudo foi delineado para verificar se protótipos de mini-implantes (PMI) desenvolvidos para a ancoragem esquelética do aparelho de Herbst são capazes de suportar forças ortopédicas e, também, determinar a variação da força de flexão desses PMI de acordo com o local de inserção (maxila ou mandíbula). MÉTODOS: após o cálculo do tamanho da amostra, 13 PMI foram colocados em três cadáveres de Minipigs br1 (seis na maxila e sete na mandíbula). Os corpos de prova foram preparados e submetidos a um teste mecânico. Cálculos da média e o do desvio-padrão foram realizados para cada região. O teste t de Student para duas amostras não pareadas foi utilizado para comparar a resistência dos PMI entre as regiões de inserção. O teste t de Student para uma amostra foi realizado para o teste de hipótese. Foram consideradas forças ortopédicas aquelas acima de 1,0kgf. RESULTADOS: os PMI foram capazes de suportar forças de flexão maiores que 1,0kgf (13,8 ± 2,3Kg na região posterior da maxila, e 20,5 ± 5,2Kg na região anterior da mandíbula), apresentando significativa menor força de flexão na região anterior da mandíbula (p < 0,05). CONCLUSÃO: os PMI são capazes de suportar forças ortopédicas, sendo mais resistentes quando utilizados na região anterior da mandíbula do que na posterior da maxila, em cadáveres de Minipigs br1.

Properties of Composite Materials Used for Bracket Bonding

The purpose of this study was to evaluate in vitro the shear bond strength to enamel, flexural strength, flexural modulus, and contraction stress of one orthodontic composite and two flowable composites. Orthodontic brackets were bonded to 45 human maxillary premolars with the composites Transbond XT, Filtek Z-350 flow and Opallis flow and tested for shear bond strength. For measurement of flexural strength and flexural modulus, specimens were fabricated and tested under flexion. For the contraction stress test, cylindrical specimens were tested and an extensometer determined the height of the specimens. The data were subjected to one-way ANOVA and Tukey's test (α=0.05). The shear bond strength values were significantly lower (p<0.05) for the flowable composites compared with the orthodontic composite. For the flexural strength, no statistically significant difference was found among the composites (p>0.05) while the flexural modulus was significantly higher (p<0.05) for Transbond XT than for Filtek Z-350 flow and Opallis flow. The orthodontic composite presented significantly lower contraction stress values than the flowable composites (p<0.05). The light-activated orthodontic composite material presented higher flexural modulus and shear bond strength and lower contraction stress than both flowable composites.

O objetivo desse estudo foi avaliar a resistência ao cisalhamento no esmalte, resistência flexural, módulo flexural, tensão de contração de polimerização de duas resinas flow e uma resina ortodôntica. Os bráquetes ortodônticos foram colados em 45 pré-molares humanos e divididos: Transbond XT, Filtek Z-350 flow, Opallis flow e testado para resistência ao cisalhamento (n=15). Para a resistência e módulo flexural espécimes foram confeccionados e testados sob flexão. Para o teste de tensão de contração de polimerização, espécimes cilíndricos foram confeccionados e monitorados com um extensômetro (Instron). Os dados foram submetidos aos testes ANOVA a um critério e Tukey (α=0,05) para contraste de média. (n=15). A resistência de união das resinas flow foram significantemente menos que o da resina ortodôntica (p>0,05). A resistência flexural não demonstrou diferença significante entre os grupos testados (p>0,05). O módulo flexural da resina ortodôntica foi significantemente maior que o grupo das resinas flow (p<0,05). A tensão de contração de polimerização da resina ortodôntica foi significantemente menor (p<0,05). A resina ortodôntica obteve os maiores valores de resistência de união ao cisalhamento, resistência flexural e a menor tensão de contração de polimerização quando comparada as resinas flow testadas.

Effect of Sealant Application and Thermal Cycling on Bond Strength of Tissue Conditioners to Acrylic Resin

The aim of this study was to evaluate the effect of sealer application and thermal cycling on the bond strength between tissue conditioners and acrylic resin, and to observe the type of bond failure. Two hundred eighty-eight specimens (10x16x3 mm) were made of an acrylic resin (Lucitone 500, Dentsply) using a metal muffle. Specimens were divided into four groups according to the tissue conditioner (Coe-Comfort, GC or Dentusoft, Densell) used and whether or not a sealer (Eversoft Soft Liner Sealer, Myerson) was applied. Each of the four groups was subdivided into other six subgroups (n=12) to undergo thermocycling for 45, 90, 135, 180 or 210 cycles with a dwell time of 60 s, or to be left non thermocycled (control). Tensile bond strength was measured in a universal testing machine at a crosshead speed of 5 mm/min. Sealant application had no effect on the tensile bond strength of the relined acrylic resin, regardless of the tissue conditioner used (Coe-Comfort: p=0.306 and Dentusoft: p=0.1501). The number of thermal cycles had a significant effect on the tensile bond strength of the relined acrylic resin (Coe-Comfort: p=0.002 and Dentusoft: p<0.001). Both tissue conditioners presented similar bond strength to acrylic resin. For both tissue conditioners, sealer coatings had no influence on bond strength, while different numbers of thermal cycles affected that mechanical property.

Os objetivos deste estudo foram avaliar o efeito da aplicação de selante e a ciclagem térmica na resistência de união entre condicionadores de tecido e resina acrílica e observar o padrão de fratura. Duzentos e oitenta e oito espécimes (10×16×3 mm) de resina acrílica (Lucitone 500, Dentsply) foram confeccionados utilizando-se uma mufla metálica. Os espécimens foram divididos em quatro grupos de acordo com o condicionador de tecido (Coe-Comfort, GC ou Dentusoft, Densell) e com o uso ou não de selante (Eversoft Soft Liner Sealer, Myerson). Cada um dos quatro grupos foi subdividido em seis grupos para a realização de 45, 90, 135, 180 ou 210 ciclos térmicos, ou ausência de termociclagem (controle). Resistência de união por tração foi mensurada em uma máquina universal de ensaios com velocidade de 5 mm/min. A aplicação de selante não afetou a resistência de união por tração da resina acrílica reembasada, independentemente do condicionador de tecido utilizado (Coe-Comfort: p=0,306 e Dentusoft: p=0,1501). O número de ciclos térmicos apresentou efeito significativo na resistência de união por tração da resina acrílica reembasada (Coe-Comfort: p=0,002 e Dentusoft: p<0,001). Ambos os condicionadores de tecidos apresentaram resistência de união semelhante à resina acrílica. Para ambos os condicionadores de tecidos, a aplicação de selante não apresentou influência na resistência de união, enquanto que diferentes números de ciclos térmicos afetaram essa propriedade mecânica.

Evaluation of the friction force generated by monocristalyne and policristalyne ceramic brackets in sliding mechanics

OBJECTIVE: To evaluate and compare "in vitro" the maximum friction force generated by three types of esthetic brackets, two types of polycrystalline conventional ceramic brackets (20/40 and InVu) and one type of sapphire monocrystalline bracket (Radiance) in dry and artificial saliva wet settings. Also, to evaluate the influence exerted by artificial saliva on the friction forces of those brackets. METHODS: Tests were performed in dry and artificial saliva wet setting (Oral Balance) by using an EMIC DL 10000 testing machine, simulating a 2 mm slide of 0.019 x 0.025-in rectangular stainless steel wires over the pre-angulated and pre-torqued (right superior canine, Roth prescription, slot 0.022 x 0.030-in) brackets (n = 18 for each bracket). In order to compare groups in dry and wet settings, the ANOVA was used. For comparisons related to the dry versus wet setting, the student t test was used for each group. RESULTS: The results showed that in the absence of saliva the Radiance monocrystalline brackets showed the highest friction coefficients, followed by the 20/40 and the InVu polycrystalline brackets. In tests with artificial saliva, the Radiance and the 20/40 brackets had statistically similar friction coefficients and both were greater than that presented by the InVu brackets. The artificial saliva did not change the maximum friction force of the Radiance brackets, but, for the others (20/40 and InVu), an increase of friction was observed in its presence. CONCLUSION: The InVu brackets showed, in the absence and in the presence of saliva, the lowest friction coefficient.

OBJETIVO: avaliar e comparar in vitro as cargas máximas de atrito geradas por três tipos de braquetes estéticos, sendo dois deles cerâmicos policristalinos convencionais (20/40 e InVu) e um monocristalino de safira (Radiance), em ambientes seco e umedecido por saliva artificial. Também avaliar a influência exercida pela saliva artificial sobre as cargas de atrito dos referidos braquetes. MÉTODOS: os ensaios foram realizados em ambiente seco e em ambiente umedecido com saliva artificial em gel (Oral Balance), utilizando uma máquina de ensaios mecânicos (EMIC, modelo DL10000), simulando um deslizamento de 2mm de fios retangulares 0,019" x 0,025" de aço sobre os braquetes (n = 18, para cada braquete), pré-angulados e pré-torqueados (canino superior direito prescrição Roth, slot 0,022" x 0,030"). Para comparação entre os braquetes, em ambiente seco ou umedecido, utilizou-se a análise de variância; e para a comparação dos braquetes em ambiente seco e umedecido, utilizou-se o teste t para amostras independentes. RESULTADOS: os resultados obtidos indicaram que, na ausência de saliva, os braquetes monocristalinos Radiance demonstraram o maior coeficiente de atrito, seguidos pelos braquetes policristalinos 20/40 e InVu. Nos ensaios realizados em ambiente umedecido, os braquetes Radiance e 20/40 apresentaram coeficientes de atrito estatisticamente semelhantes, e superiores ao apresentado pelos braquetes InVu. A saliva artificial não promoveu alterações na força máxima de atrito para os braquetes Radiance; todavia, para os demais (20/40 e InVu), promoveu aumento significativo nos coeficientes de atrito. CONCLUSÃO: os braquetes InVu apresentaram, tanto nos ensaios realizados na ausência, quanto na presença de saliva, os menores coeficientes de atrito, entre os braquetes ensaiados.

Macro design effects on stress distribution around implants: A photoelastic stress analysis.

Objectives: Biomechanics is one of the main factors for achieving long-term success of implant supported prostheses. Long-term failures mostly depend on biomechanical complications. It is important to distinguish the effects of macro design of the implants. Materials and Methods: In this study, the photoelastic response of four different types of implants that were inserted with different angulations were comparatively analyzed. The implant types investigated were screw cylinder (ITI, Straumann AG, Basel, Switzerland), stepped cylinder (Frialit2, Friadent GmbH, Manheim, Germany), root form (Camlog Rootline, Alatatec, Wilshelm, Germany), and cylindrical implant, with micro-threads on the implant neck (Astra, AstraTech, Mölndal, Sweden). In the test models, one of the implants was inserted straight, while the other one was aligned mesially with 15° angles. The superstructures were prepared as single crowns. A 150N loading was applied to the restorations throughout the test. Results: A comparison of the implant designs showed that there were no significant differences between the straight implants; however, between the inclined implants, the most favorable stress distribution was seen with the stepped cylinder implants. The least favorable stress concentration was observed around the root formed implants. Microthreads around the implant neck appeared to be effective in a homogenous stress distribution. Observations showed that misaligned implants caused less stress than straight implants, but the stress concentrations were not homogenous. Conclusion: As there were observable differences between the implant types, straight placed cylindrical implants showed better stress distribution characteristics, while inclined tapering implants had better stress distribution characteristics.

The effect of air abrasion on the retention of metallic brackets bonded to fluorosed enamel surface.

Background: Bonding brackets to fluorosed enamel remains a clinical challenge and bracket failure at the compromised enamel interface is common. Objective: To check the effect of air abrasion on the retention of metallic brackets bonded to fluorosed enamel surface. Materials and Methods: Sixty freshly extracted human premolar teeth having moderate to severe dental fluorosis as per Dean's criteria were collected and divided into three groups of 20 each. The groups were treated as follows: In group I, acid etching was followed by bonding with Transbond XT® ; in group II, sandblasting and acid etching was followed by bonding with Transbond XT® ; and in group III, sandblasting and acid etching was followed by bonding with Enlight LC® . An Instron™ universal testing machine was used for determining the debonding force, and from this the shear bond strength was computed. The sample with highest shear bond strength from each group was selected for the scanning electron microscopy (SEM) study. The prepared specimens were examined under a JSM-840A scanning electron microscope (JEOL Ltd, Tokyo, Japan) operated at 20 kV. Photographs were taken at progressively higher magnifications of ×50, ×100, ×500, and ×1000 to view the enamel surface and the adhesive remaining on the enamel surface after debonding. The shear bond strengths of the groups were compared using the one-way ANOVA (analysis of variance) and Tukey post hoc test. The distribution of adhesive remnant index (ARI) score was compared using the Chi-square test. Results: The mean shear bond strength in group I was 10.36 MPa, with a standard deviation of 0.225. The corresponding values in group II and group III were 11.41±0.237 MPa and 11.39±0.201 Mpa, respectively. There was a statistically significant difference between the three groups in the mean shear bond strength values. Conclusion: Sandblasting followed by acid etching provides significantly higher bond strength values compared to acid etching alone, irrespective of the bonding material employed.